Chimei Polylac PA 758 transparent ABS pellet Description
Polylac PA758 is a methyl methacrylate-butadiene-styrene copolymer, also known as MABS, produced by Chimei Corporation. This is an ABS material with excellent transparency and a melt index of 3.0g/10min (at 200℃ 5kg). PA758 MABS material has high flow speed and rapid molding characteristics, which facilitates the large-scale production of ABS products.
Key Attributes
| Chimei Polylac MABS PA-758 |
| Product information |
| Manufacturer |
CHIMEI CORPORATION |
| Other Certificates |
·RoHS ·REACH ·MSDS |
| Part Marking Code |
>MABS material< |
| Color |
Transparent Color |
| Material Shape |
MABS Pellets |
| Process |
Injection molding MABS material |
| Flame retardant |
HB |
| Material Attribute |
Injection grade |
| specification |
·RoHS ·UL |
| Features |
·High flow ·Rapid moldability ·Good moldability |
| Application |
·Office Applications ·E & E housing ·Home Appliances housing ·Washing machine housing ·Industrial Aplications
·Kitchen Appliances Applications ·Pen housing ·Stationery ·Vacuum cleaner housing ·Thin wall products
·Wearable products
|
| UL File NO. |
E56070 |
| Physical properties |
Standard |
Value |
Unit |
|
Density 23°C
|
ASTM D792
|
1.08
|
g/cm³
|
|
Density 23°C
|
ISO 1183
|
1.08
|
g/cm³
|
|
Shrinkage
|
ISO 294
|
0.3~0.7
|
%
|
|
Melt Index 200°C 5kg
|
ASTM D1238
|
3
|
g/10min
|
|
Melt Index 200°C 5kg
|
ISO 1133
|
3.0
|
cm³/10min
|
| Hardness |
Standard |
Value |
Unit |
|
Rockwell Hardness R(Scale)
|
ASTM D785
|
107
|
|
| Mechanical behavior |
Standard |
Value |
Unit |
| Tensile Strength Yield 6mm/min |
ASTM D638 |
405 |
kg/cm² |
| Tensile Strength Yield 50mm/min |
ISO 527 |
42 |
Mpa |
| Tensile Strength Break 50mm/min |
ISO 527 |
33 |
MPa |
| Elongation 6mm/min |
ASTM D638 |
40 |
% |
| Elongation 50mm/min |
ISO 527 |
40 |
% |
| Flexural Strength 2.8mm/min |
ASTM D790 |
550 |
kg/cm² |
| Flexural Strength 2.0mm/min |
ISO 178 |
57 |
Mpa |
| Flexural Modulus 2.8mm/min |
ASTM D790 |
19000 |
kg/cm² |
| Flexural Modulus 2.0mm/min |
ISO 178 |
1.9 |
GPa |
| Izod Notch Impact 23°C 6.4mm |
ASTM D256 |
16 |
kg-cm/cm |
| Izod Notch Impact 23°C 3.2mm |
ASTM D256 |
15 |
kg-cm/cm |
| Izod Notch Impact 23°C |
ISO 180 |
14 |
kJ/m² |
| Izod Notch Impact -30°C |
ISO 180 |
7 |
kJ/m² |
| Charpy Notch Impact 23°C |
ISO 179 |
14 |
kJ/m² |
| Charpy Notch Impact -30°C |
ISO 179 |
7 |
kJ/m² |
| Thermal |
Standard |
Value |
Unit |
| Heat deflection temperature (HDT) Annealed 1.8MPa |
ASTM D648 |
99 |
°C |
| Heat deflection temperature (HDT) Unannealed 1.8MPa |
ASTM D648 |
88 |
°C |
| Heat deflection temperature (HDT) Unannealed 1.8MPa |
ISO 75 |
77 |
°C |
| Heat deflection temperature (HDT) Unannealed 1.8MPa |
ISO 75 |
97 |
°C |
| Vicat Softening Temperature 50°C/hr 10N |
ASTM D1525 |
105 |
°C |
| Vicat Softening Temperature 50°C/hr 10N |
ISO 306 |
104 |
°C |
| Vicat Softening Temperature 50°C/hr 50N |
ISO 306 |
96 |
°C |
| CLE |
ISO 11359 |
9.3E-5 |
cm/cm/°C |
| Flammability |
Standard |
Value |
Unit |
| Flame Rating All Color 1.5mm |
UL94 |
HB |
|
| Flame Rating All Color 3.0mm |
UL94 |
HB |
|
⚠️The technical data sheet (TDS) of Chimei PA 758 transparent ABS material from Chimei corporation, if there are differences, please refer to the official website of Chimei.
Chimei PA 758 transparent ABS pellet Advantage
- Excellent transparency. Chimei Polylac PA 758 uses methyl methacrylate to replace acrylonitrile in ABS material, and copolymerizes it with butadiene and styrene to give the material excellent transparency. It is suitable for applications with high requirements on appearance properties, transparency and transmittance.
- Good processing performance. Chimei PA758 transparent ABS material has a melt index of 3g/10min under a 200℃ 5kg test environment, which is suitable for conventional injection molding processing. Its good fluidity is suitable for the production of thin-walled products such as pen shells and stationery shells.