Teijin Panlite L-1250Y PC Description
Panlite L-1250Y is a general purpose polycarbonate (PC material) produced by Teijin Chemicals Co., Ltd. It has medium viscosity and good foaming properties, can be processed by injection molding and extrusion molding and has a wide range of applications.
|
Teijin Panlite L-1250Y PC
|
|
Product information
|
|
Manufacturer
|
Teijin chemical LTD.
|
|
Part Marking Code
|
>PC material<
|
|
Color
|
Transparent
|
|
Material Shape
|
PC pellets
|
|
Process
|
·Injection molding ·Extrusion molding
|
|
Viscosity
|
Medium viscosity
|
|
Flame retardant
|
HB V-2
|
|
specification
|
·RoHS ·UL ·UL-746C F2
|
|
Features
|
·Transparency ·Good mould release
|
|
Additives
|
Mold release
|
|
Application
|
General purpose
|
|
Physical property
|
Standard
|
Value
|
Unit
|
|
Density
|
ISO 1183
|
1.2
|
g/cm³
|
|
Shrinkage xFlow 4.0mm
|
Internal method
|
0.5~0.7
|
%
|
| Water absorption 23℃ 1.2kg |
ISO 62 |
0.20 |
% |
|
Melt Index 300°C 1.2kg
|
ISO 1133
|
8
|
cm³/10 min
|
|
Mechanical behavior
|
Standard
|
Value
|
Unit
|
|
Tensile Modulus
|
ISO 527
|
2400
|
MPa
|
|
Tensile Strength Yield
|
ISO 527
|
61.0
|
MPa
|
|
Elongation yield
|
ISO 527
|
6.0
|
%
|
|
Elongation break
|
ISO 527
|
50
|
%
|
|
Flexural Strength 2.0mm/min
|
ISO 178
|
91
|
Mpa
|
|
Flexural modulus 2.0mm/min
|
ISO 178
|
2300
|
Mpa
|
|
Charpy Notch Impact
|
ISO 179
|
76
|
kJ/㎡
|
|
Charpy Un-notch Impact
|
ISO 179
|
NB
|
kJ/㎡
|
|
Optical
|
Standard
|
Value
|
Unit
|
|
Transmittance
|
ASTM D1003 |
88 |
% |
| Refractive |
ASTM D542 |
1.585 |
|
|
Thermal
|
Standard
|
Value
|
Unit
|
|
Heat deflection temperature (HDT) unannealed 0.45Mpa
|
ISO 75 |
142
|
℃
|
|
Heat deflection temperature (HDT) unannealed 1.8 Mpa
|
ISO 75
|
129
|
℃
|
|
Vicat softending temperature 50℃/hr 50N
|
ISO 306 |
149
|
℃
|
|
CLE Flow
|
ISO 11359
|
7E-5 |
cm/cm/℃
|
| CLE xFlow |
ISO 11359 |
7E-5 |
cm/cm/℃ |
|
Flammability
|
Standard
|
Value
|
Unit
|
|
Flame Rating All color 1.5mm
|
UL94
|
HB
|
|
|
Flame Rating All color 3.0mm
|
UL94
|
HB
|
|
⚠️The technical data sheet of Teijin Panlite L-1250Y polycarbonate, from Teijin chemical, if there are differences, please refer to the official website of Teijin chemical.
Teijin L-1250Y Panlite PC Advantage
-
Highly transparent polycarbonate material, Teijin Panlite L-1250Y is a highly transparent PC pellet with better transparency, transmittance, and refractive index than its competitors, used for applications that require a high level of appearance.
-
Excellent processing performance. Panlite L-1250Y PC has a melt index of 8 cm³/10 min at 300°C (1.2 kg). This high melt index is suitable for the production of complex and precise parts. L-1250Y polycarbonate also contains a release agent, which reduces material residue in the mold and improves production efficiency.
Why choose us as Teijin Panlite L-1250Y PC pellets supplier?
- Leading Polycarbonate resin pellets supplier (PC material) , 10+ years of experience in plastic product manufacturing and chemical raw material import and export
- Fastest Arrival, with warehouses in multiple ports
- 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 10+ years
- Free Samples for production testing
- Wholesale price, even a piece of goods is based on the wholesale price
Relacionado